Effect of ZrO2 Addition on the Properties of CuMn2/Al-Ti Monolithic Catalysts for Benzene Catalytic Combustion

ZHANG Zhiqiang1,2, HE Zhanfeng1,2, WANG Juanyun1, WANG Huanyi1,2, LI Jihua1,2, JIANG Yi1,*, CHEN Junhe1, ZHANG Xiaoxia1   

  1. 1Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences, Chengdu 610041, Sichuan, China 2Graduate University of Chinese Academy of Sciences, Beijing 100049, China
  • Received:2010-07-25 Online:2010-07-25 Published:2010-07-25

Abstract: A series of MnOx/Al0.82Ti0.18Ox (Mn/Al-Ti), Cu/Al-Ti, CuMn2/Al-Ti, and CuMn2Zr1.25/Al-Ti monolithic catalysts were prepared by the wet impregnation method. X-ray diffraction, X-ray photoelectron spectroscopy, H2 temperature-programmed reduction, and N2 adsorption were used to characterize the catalysts. The results showed that the addition of ZrO2 in the catalysts increases the specific surface area, component dispersion, oxygen species concentration on the surface, and the redox ability of the catalysts. The monolithic catalysts have high catalytic activity, and the benzene conversion of 91% was obtained at temperature as low as 281 oC.

Key words: copper oxide, manganese oxide, zirconia, monolithic catalyst, catalytic combustion, benzene