平板结构高效钙钛矿太阳能电池的旋涂溶液溶剂工程

doi:10.1016/S1872-2067(15)60929-9

催化学报 ›› 2015, Vol. 36 ›› Issue (8): 1183-1190.DOI: 10.1016/S1872-2067(15)60929-9

平板结构高效钙钛矿太阳能电池的旋涂溶液溶剂工程

蔡冰^a,b, 张文华^b, 邱介山^a

a 大连理工大学, 精细化工国家重点实验室, 能源材料化工辽宁省重点实验室, 碳素材料实验室, 辽宁大连116024;
b 中国科学院大连化学物理研究所催化基础国家重点实验室, 洁净能源国家实验室, 辽宁大连116023

收稿日期:2015-05-21 修回日期:2015-06-16 出版日期:2015-07-29 发布日期:2015-07-30
通讯作者: 邱介山
基金资助:
国家自然科学基金(21336001, 20873141).

Solvent engineering of spin-coating solutions for planar-structured high-efficiency perovskite solar cells

Bing Cai^a,b, Wen-Hua Zhang^b, Jieshan Qiu^a

a Carbon Research Laboratory, Liaoning Key Laboratory for Energy Materials and Chemical Engineering, State Key Laboratory of Fine Chemicals, Dalian University of Technology, Dalian 116024, Liaoning, China;
b State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian National Laboratory for Clean Energy, Dalian 116023, Liaoning, China

Received:2015-05-21 Revised:2015-06-16 Online:2015-07-29 Published:2015-07-30
Supported by:
This work was partly supported by the National Natural Science Foundation of China (21336001, 20873141).

摘要/Abstract

摘要：

自2009年首次应用于太阳能电池中以来, 有机铅卤化物钙钛矿材料得到了极大关注. 据文献报道, 有机铅卤化物钙钛矿材料在不同结构的太阳能电池中都得到了应用, 其中与有机太阳能电池类似的平板结构钙钛矿具有结构简单、制备容易等优点, 非常适合用于柔性电池和多节电池等各种应用. 在平板结构的太阳能电池中, 制备高质量的钙钛矿薄膜至关重要. 真空热蒸镀法虽然可以制备厚度均匀的钙钛矿薄膜, 获得高的器件性能, 但是设备成本较高, 不利于大规模生产. 而在溶液法中, 早期的一步旋涂法和两步法由于没有多孔金属氧化物的支撑, 很难制备均匀的钙钛矿平板薄膜; 而气相辅助的两步法虽然制备的薄膜比较均匀, 但反应时间却比较长. 程一兵研究组采用在旋涂N,N-二甲基甲酰胺(DMF)溶液时滴加氯苯使钙钛矿快速析出结晶的方法, 制备了高质量的均匀的CH₃NH₃PbI₃薄膜. Seok研究组采用1,4-丁内酯(GBL)和二甲基亚砜(DMSO)的混和溶剂, 在旋涂时滴加甲苯的方法, 在多孔二氧化钛上也制得了均匀的CH₃NH₃PbI₃薄膜, 取得了很高转化效率(16.7%), 但缺少对不同溶剂比例的细致研究, 另外, 也没有对平板结构电池性能进行研究. 本文采用DMF-DMSO和GBL-DMSO作为混合溶剂在二氧化钛致密层上旋涂制备了平板结构的钙钛矿薄膜, 并且对混合溶剂的比例对器件性能的影响进行了详细的考察和优化. 当纯DMF或纯GBL作为旋涂溶剂时, 得到的CH₃NH₃PbI₃钙钛矿薄膜含有大量不连续的晶粒, 表面的覆盖度很差, 对入射光的吸收远弱于连续均匀的薄膜. 而且XRD结果表明, 纯DMF或纯GBL作为旋涂溶剂的薄膜残留有前驱体的杂质, 对器件性能非常不利. 而采用DMSO作为旋涂溶剂时, 制得的薄膜表面则比较均匀, 几乎达到100%的覆盖. 这主要是由于在旋涂溶液中形成了PbI₂-CH₃NH₃I-DMSO的中间相, 这样可以避免纯DMF或纯GBL溶剂蒸发时PbI₂和CH₃NH₃I的剧烈反应, 因此退火后制得的CH₃NH₃PbI₃薄膜非常均匀. 然而由于纯DMSO的高粘度和低挥发速度, 并不是非常适合作为旋涂溶剂, 因此我们将DMF和GBL加入到DMSO中形成混合溶剂来考察对制备的钙钛矿薄膜质量和器件性能的影响. 扫描电镜结果表明, 加入20%~40%体积分数的DMF时, 形成的薄膜表面非常均匀而且晶粒尺寸很大, 达到微米级别, 这样有利于减少晶界处的复合, 提高电池性能. 继续增加DMF比例会导致晶粒减小, 晶界和孔隙增多, 薄膜表面也更加粗糙. 而加入GBL时得到的晶粒要远小于加入DMF时的尺寸, 并且随着GBL比例的增加, 薄膜的表面变得更加粗糙, 孔隙明显增多, 严重影响电池性能. XRD结果表明, 纯DMSO和混合溶剂制得的薄膜都没有前驱体的残留. 紫外可见吸收光谱表明, 随着DMF比例的增加, 吸收逐渐增强; 而随着GBL比例的增加, 吸收逐渐减弱. 这主要由于不同比例溶剂制得的薄膜厚度有所差异造成的.由相关的薄膜制备的平板结构太阳能电池I-V测试表明: 当使用DMF-DMSO混合溶剂时, 随着DMF比例由0%增至40%, 短路电流和开路电压逐渐增加, 填充因子略微减小, 总体上导致光电转化效率逐渐增大. 随着DMF继续增多, 开路电压和填充因子的减小导致转化效率逐渐降低. 而当使用GBL-DMSO混合溶剂时, 主要受到短路电流的影响, 电池的效率明显低于含DMF的混合溶剂的情况, 而且随着GBL增多, 电池效率逐渐降低. 电池的最高转化效率达到了16.5%, 最高功率点下固定电压扫描得到的稳态效率也达到了14.4%, 高于报道中采用类似结构的电池的性能. 由于在整个电池制备过程中, 整个实验过程都低于100 ℃, 该方法非常适合未来推广到柔性太阳能电池和多节太阳能电池上.

关键词: 钙钛矿, 薄膜, 太阳能电池, 溶剂工程, 形貌, 器件性能

Abstract:

Control of the morphology and coverage of high-quality perovskite films is the main issue affecting planar-structured perovskite solar cells fabricated by solution processing. In this work, the solvent engineering of mixed solutions for spin-coating uniform perovskite thin films was investigated in detail by adding different ratios of N,N-dimethylformamide (DMF) or γ-butyrolactone (GBL) to dimethyl sulfoxide (DMSO). The morphology and film thickness of the resulting perovskite films were found to be significantly altered. At 20%~40% (volume fraction) of N,N-dimethylformamide mixed with DMSO, micrometer scale grains and reduced grain boundaries were observed on the highly uniform perovskite thin films. The optimized planar-structured perovskite solar cells showed power conversion efficiency as high as 16.5% and a stabilized efficiency of 14.4% at a fixed forward bias of 0.88 V.

Key words: Perovskite, Film, Solar cell, Solvent engineering, Morphology, Device performance

蔡冰, 张文华, 邱介山. 平板结构高效钙钛矿太阳能电池的旋涂溶液溶剂工程[J]. 催化学报, 2015, 36(8): 1183-1190.

Bing Cai, Wen-Hua Zhang, Jieshan Qiu. Solvent engineering of spin-coating solutions for planar-structured high-efficiency perovskite solar cells[J]. Chinese Journal of Catalysis, 2015, 36(8): 1183-1190.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(15)60929-9

https://www.cjcatal.com/CN/Y2015/V36/I8/1183

参考文献

[1] Kojima A, Teshima K, Shirai Y, Miyasaka T. J Am Chem Soc, 2009, 131: 6050
[2] Lee M M, Teuscher J, Miyasaka T, Murakami T N, Snaith H J. Science, 2012, 338: 643
[3] Noh J H, Im S H, Heo J H, Mandal T N, Seok S I. Nano Lett, 2013, 13: 1764
[4] Jeon N J, Noh J H, Yang W S, Kim Y C, Ryu S, Seo J, Seok S I. Nature, 2015, 517: 476
[5] Zuo F, Williams S T, Liang P-W, Chueh C-C, Liao C-Y, Jen A K-Y. Adv Mater, 2014, 26: 6454
[6] Heo J H, Im S H, Noh J H, Mandal T N, Lim C S, Chang J A, Lee Y H, Kim H J, Sarkar A, Nazeeruddin M K, Gratzel M, Seok S I. Nat Photonics, 2013, 7: 487
[7] Cai B, Xing Y D, Yang Z, Zhang W H, Qiu J S. Energy Environ Sci, 2013, 6: 1480
[8] Jeon N J, Lee J, Noh J H, Nazeeruddin M K, Gratzel M, Seok S I. J Am Chem Soc, 2013, 135: 19087
[9] Ryu S C, Noh J H, Jeon N J, Kim Y C, Yang S, Seo J W, Seok S I. Energy Environ Sci, 2014, 7: 2614
[10] Cai B, Zhong D, Yang Z, Huang B K, Miao S, Zhang W H, Qiu J S, Li C. J Mater Chem C, 2015, 3: 729
[11] Xu Y Z, Shi J J, Lv S T, Zhu L F, Dong J, Wu H J, Xiao Y, Luo Y H, Wang S R, Li D M, Li X G, Meng Q B. ACS Appl Mater Interfaces, 2014, 6: 5651
[12] Kim H S, Lee C R, Im J H, Lee K B, Moehl T, Marchioro A, Moon S J, Humphry-Baker R, Yum J H, Moser J E, Graetzel M, Park N G. Sci Rep, 2012, 2: 591
[13] Mei A Y, Li X, Liu L F, Ku Z L, Liu T F, Rong Y G, Xu M, Hu M, Chen J Z, Yang Y, Gratzel M, Han H W. Science, 2014, 345: 295
[14] Liu L F, Mei A Y, Liu T F, Jiang P, Sheng Y S, Zhang L J, Han H W. J Am Chem Soc, 2015, 137: 1790
[15] Shi J J, Dong J, Lv S T, Xu Y Z, Zhu L F, Xiao J Y, Xu X, Wu H J, Li D M, Luo Y H, Meng Q B. Appl Phys Lett, 2014, 104: 063901
[16] Zhong D, Cai B, Wang X L, Yang Z, Xing Y D, Miao S, Zhang W H, Li C. Nano Energy, 2015, 11: 409
[17] Liu M Z, Johnston M B, Snaith H J. Nature, 2013, 501: 395
[18] Marchioro A, Teuscher J, Friedrich D, Kunst M, van de Krol R, Moehl T, Gratzel M, Moser J E. Nat Photonics, 2014, 8: 250
[19] Stranks S D, Eperon G E, Grancini G, Menelaou C, Alcocer M J P, Leijtens T, Herz L M, Petrozza A, Snaith H J. Science, 2013, 342: 341
[20] Xing G C, Mathews N, Sun S, Lim S S, Lam Y M, Gratzel M, Mhaisalkar S, Sum T C. Science, 2013, 342: 344
[21] Eperon G E, Stranks S D, Menelaou C, Johnston M B, Herz L M, Snaith H J. Energy Environ Sci, 2014, 7: 982
[22] Yang Z, Zhang W H. Chin J Catal (杨周, 张文华. 催化学报), 2014, 35: 983
[23] Liu D Y, Kelly T L. Nat Photonics, 2014, 8: 133
[24] Docampo P, Ball J M, Darwich M, Eperon G E, Snaith H J. Nat Commun, 2013, 4: 2761
[25] Todorov T, Gershon T, Gunawan O, Sturdevant C, Guha S. Appl Phys Lett, 2014, 105: 173902
[26] Loper P, Moon S J, de Nicolas S M, Niesen B, Ledinsky M, Nicolay S, Bailat J, Yum J H, De Wolf S, Ballif C. Phys Chem Chem Phys, 2015, 17: 1619
[27] Eperon G E, Burlakov V M, Docampo P, Goriely A, Snaith H J. Adv Funct Mater, 2014, 24: 151
[28] Zhao Y X, Zhu K. J Phys Chem Lett, 2014, 5: 4175
[29] Burschka J, Pellet N, Moon S J, Humphry-Baker R, Gao P, Nazeeruddin M K, Gratzel M. Nature, 2013, 499: 316
[30] Xu Y Z, Zhu L F, Shi J J, Lv S T, Xu X, Xiao J Y, Dong J, Wu H J, Luo Y H, Li D M, Meng Q B. ACS Appl Mater Interfaces 2015, 7: 2242
[31] Chen Q, Zhou H P, Hong Z R, Luo S, Duan H S, Wang H H, Liu Y, Li G, Yang Y. J Am Chem Soc, 2014, 136: 622
[32] Du T, Wang N, Chen H J, Lin H, He H C. ACS Appl Mater Interfaces, 2015, 7: 3382
[33] Xiao M D, Huang F Z, Huang W C, Dkhissi Y, Zhu Y, Etheridge J, Gray-Weale A, Bach U, Cheng Y B, Spiccia L. Angew Chem Int Edit, 2014, 53: 9898
[34] Jeon N J, Noh J H, Kim Y C, Yang W S, Ryu S C, Seol S I. Nat Mater, 2014, 13: 897
[35] Wu Y Z, Islam A, Yang X D, Qin C J, Liu J, Zhang K, Peng W, Han L Y. Energy Environ Sci, 2014, 7: 2934
[36] Yella A, Heiniger L P, Gao P, Nazeeruddin M K, Gratzel M. Nano Letters, 2014, 14: 2591
[37] Shen D H, Yu X, Cai X, Peng M, Ma Y Z, Su X, Xiao L X, Zou D C. J Mater Chem A, 2014, 2: 20454

平板结构高效钙钛矿太阳能电池的旋涂溶液溶剂工程

Solvent engineering of spin-coating solutions for planar-structured high-efficiency perovskite solar cells

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	王元男, 王立娜, 张可新, 徐靖尧, 武倩楠, 谢周兵, 安伟, 梁宵, 邹晓新. 钙钛矿氧化物在水裂解反应中的电催化研究[J]. 催化学报, 2023, 50(7): 109-125.
[2]	李金鹏, 陈洁, 郑庆舒, 屠波, 涂涛. 配位组装构筑的磁性核壳复合材料促进CO₂高值催化转化[J]. 催化学报, 2023, 48(5): 258-266.
[3]	李卓根, 张伟斌, 朱陆军, 高健智, 石先进, 黄宇, 刘鹏, 朱刚强. 通过实验和理论验证Pt⁰/SrTiO_3‒_δ复合催化剂双反应路径促进CO₂还原[J]. 催化学报, 2023, 46(3): 113-124.
[4]	王宇, Jaime Gallego, 汪炜, Phillip Timmer, 丁敏, Alexander Spriewald Luciano, Tim Weber, Lorena Glatthaar, 郭杨龙, Bernd M. Smarsly, Herbert Over. 析出型LaFe_0.9Ru_0.1O₃钙钛矿催化剂在丙烷催化氧化反应中的自活化现象[J]. 催化学报, 2023, 54(11): 250-264.
[5]	张艳飞, 王洪, 刘䶮, 李灿. 有机-无机杂化钙钛矿基光催化剂用于可见光催化芳香族溴化反应并联产氢气[J]. 催化学报, 2022, 43(7): 1805-1811.
[6]	周莹杰, 刘天夫, 宋月锋, 吕厚甫, 刘清雪, 塔娜, 张小敏, 汪国雄. 镍高度分散在铁基钙钛矿用于高温固体氧化物电解池阴极的CO₂电催化还原研究[J]. 催化学报, 2022, 43(7): 1710-1718.
[7]	付阳, 谢起贤, 武琳晓, 罗景山. 不同预处理的氧化亚铜纳米线电极诱导的晶面效应提升电化学CO₂还原为多碳产物[J]. 催化学报, 2022, 43(4): 1066-1073.
[8]	徐阳锐, 朱晓蝶, 颜欢, 王盼盼, 宋旼珊, 马长畅, 陈自然, 储金宇, 刘馨琳, 逯子扬. 盐酸介导策略合成的具有优异光催化能力的ZnFe₂O₄小颗粒点缀一维苝二酰亚胺S型异质结[J]. 催化学报, 2022, 43(4): 1111-1122.
[9]	张琪, 陈辉, 杨岚, 梁宵, 石磊, 冯庆, 邹永存, 李国栋, 邹晓新. 非催化瞬态铱脱溶—筛选铱基钙钛矿析氧催化剂时不可忽视的实验现象[J]. 催化学报, 2022, 43(3): 885-893.
[10]	陈通, 刘丽珍, 胡程, 黄洪伟. Bi₂WO₆基光催化剂在环境和能源领域的最新研究进展[J]. 催化学报, 2021, 42(9): 1413-1438.
[11]	廖宇翔, 李俊, 张世明, 陈胜利. 高指数晶面和梯度组成的PtCu₃@Pt₃Cu@Pt纳米枝晶氧还原电催化剂性能[J]. 催化学报, 2021, 42(7): 1108-1116.
[12]	Yanan Gao, Fu-Kuo Chiang, Shaojie Li, Long Zhang, Peng Wang, Emiel J. M. Hensen. α-Fe₂O₃形貌对Au/α-Fe₂O₃催化一氧化碳氧化反应性能的影响[J]. 催化学报, 2021, 42(4): 658-665.
[13]	Steffen Cychy, Sebastian Lechler, Zijian Huang, Michael Braun, Ann Cathrin Brix, Peter Blümler, Corina Andronescu, Friederike Schmid, Wolfgang Schuhmann, Martin Muhler. 甘油氧化的光谱电化学傅里叶变换衰减全反射谱红外光谱薄膜流动池中硼酸镍层厚度的优化[J]. 催化学报, 2021, 42(12): 2206-2215.
[14]	董春燕, 周燕, 塔娜, 刘雯璐, 李名润, 申文杰. 氧化铈形貌对Pd纳米粒子分散的影响[J]. 催化学报, 2021, 42(12): 2234-2241.
[15]	胡月, 吴坚, 韩宇佳, 徐维斌, 张立, 夏雪, 黄传德, 朱燕燕, 田鸣, 苏杨, 李林, 侯宝林, 林坚, 刘汶, 王晓东. 钙钛矿介导强化的铁基氧载体脱合金-脱溶循环及其太阳能热化学CO₂裂解性能[J]. 催化学报, 2021, 42(11): 2049-2058.