{111}晶面暴露对介孔金红石TiO2单晶光催化产氢的促进作用

doi:10.1016/S1872-2067(15)60996-2

催化学报 ›› 2015, Vol. 36 ›› Issue (12): 2103-2108.DOI: 10.1016/S1872-2067(15)60996-2

{111}晶面暴露对介孔金红石TiO₂单晶光催化产氢的促进作用

吴亭亭^a, 康向东^a, Mohammad W. Kadi^b, Iqbal Ismail^b, 刘岗^a, 成会明^a,b

a 中国科学院金属研究所沈阳材料科学国家(联合)实验室, 辽宁沈阳 110016;
b 阿普杜勒阿齐兹国王大学理学院化学系, 吉达 21589, 沙特阿拉伯

收稿日期:2015-08-28 修回日期:2015-09-24 出版日期:2015-12-02 发布日期:2015-12-07
通讯作者: 刘岗, Mohammad W. Kadi
基金资助:
国家重点基础研究发展计划(973计划,2014CB239401); 国家自然科学基金(51422210,51172243); 阿普杜勒阿齐兹国王大学院长科研基金(50-130-35-HiCi).

Enhanced photocatalytic hydrogen generation of mesoporous rutile TiO₂ single crystal with wholly exposed {111} facets

Tingting Wu^a, Xiangdong Kang^a, Mohammad W. Kadi^b, Iqbal Ismail^b, Gang Liu^a, Hui-Ming Cheng^a,b

a Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China;
b Chemistry Department, Faculty of Science, King Abdulaziz University, Jeddah 21589, Saudi Arabia

Received:2015-08-28 Revised:2015-09-24 Online:2015-12-02 Published:2015-12-07
Supported by:
This work was supported by the National Basic Research Program of China (973 Program, 2014CB239401), the National Natural Science Foundation of China (51422210, 51172243), and the Deanship of Scientific Research (50-130-35-HiCi), King Abdulaziz University.

摘要/Abstract

摘要：

光催化反应发生在半导体材料的表面,材料表面的原子/电子结构直接影响光催化剂的活性或选择性.因此,发展具有特定晶面的半导体光催化剂受到各国学者的普遍关注,被认为是调控光催化材料性能的有效途径之一.自2008年yang等首次合成高表面能{001}晶面占优的锐钛矿TiO₂单晶以来,控制合成暴露不同晶面TiO₂晶体的研究得到了迅猛的发展,已发展了多种方法合成了具有不同晶面的TiO₂晶体.研究表明,选择性地暴露特定的活性晶面能够显著地提高光催化剂的活性或者改变光催化反应的选择性.但是,含有完整晶面构型的TiO₂单晶样品的颗粒尺寸一般都较大,通常为几微米,因而显著增加了光生载流子传输与分离的难度,并且导致材料较小的比表面积,限制了对光催化活性的进一步提高.能否在合成含特定晶面单晶的同时增加多孔结构成为有效解决这一问题的关键.最近,Crossland等采用晶种模板法成功合成了介孔的锐钛矿TiO₂单晶,并且通过光电器件研究证实了采用该思路可进一步提高材料的光电性能.金红石TiO₂在光催化全分解水方面具有独特的优势,然而关于多孔单晶金红石TiO₂的研究相对较少,尤其是合成热力学不稳定的高表面能{111}晶面完全暴露的多孔金红石单晶面临较大的技术挑战因而一直未见文献报道.
本文利用晶种模板法, 以TiCl₄溶液为含Ti前驱体、NaF为形貌控制剂、采用水热处理制备出不同比例{111}晶面的介孔金红石单晶.我们前期工作表明,NaF可作为形貌控制剂合成低表面能{110)晶面占优的介孔金红石单晶.本文发现,通过改变NaF的添加量,可有效调变{111}/{110}晶面比例,最终合成完全暴露{111}高表面能的介孔金红石TiO₂单晶.扫描电镜结果显示,当添加20mgNaF时,合成{110}占优的具有高长径比的介孔晶体;当NaF用量增加到40mg时{110}晶面进一步缩短;至80mg时则制备出{111})高能面完全暴露的金红石TiO₂晶体.值得注意的是,对比研究表明,不采用模板合成了与多孔晶体完全相对应的不同{111}/(110}晶面比例的实心金红石晶体.透射电镜及选区电子衍射以及结合X射线衍射进一步证实,多孔的金红石TiO₂晶体与实心金红石单晶均都为单晶结构,孔结构贯穿于样品内部且具有较高的晶面结晶性.氮气吸附实验发现,虽然三个不同晶面比例介孔金红石单晶样品间的形貌具有显著的差异,但比表面积非常相近(分别为24,25,28m²/g),孔径也都为50nm左右,该值与所用SiO₂模板球的直径以及TEM观察结果相一致.光催化产氢性能结果表明,选择性的暴露活性晶面显著提高了光催化活性,仅含高能面{111}的介孔金红石单晶样品具有最高的产氢速率(约800μmolh^-1g^-1),比常规{110}晶面占优的介孔单晶样品速率提高了约一倍.尤其比实心单晶样品的产氢速率提高了至少一个数量级,这应归结于介孔结构特性所导致的表面反应活性位增加、电子传输距离缩短以及光吸收增强协同作用的结果.

关键词: 二氧化钛, 光催化剂, 介孔, 单晶, 产氢

Abstract:

The development of semiconductor photocatalysts with highly reactive facets exposed has great potential to improve their photocatalytic reactivity. We report the synthesis of mesoporous rutile TiO₂ single crystals with tunable ratios of {110} and {111} facets through the seeded-template hydrothermal method. With increasing the amount of morphology controlling agent NaF, the facet ratio of {111} to {110} increases, and eventually the mesoporous rutile TiO₂ single crystals with wholly exposed {111} reactive facets are obtained. The resultant faceted mesoporous single crystals exhibit a superior photocatalytic performance of hydrogen evolution to mesoporous single crystals with a large percentage of thermodynamically stable {110} facets, as well as the solid rutile single crystals.

Key words: Titania, Photocatalyst, Mesoporous, Single-crystal, Hydrogen generation

吴亭亭, 康向东, Mohammad W. Kadi, Iqbal Ismail, 刘岗, 成会明. {111}晶面暴露对介孔金红石TiO₂单晶光催化产氢的促进作用[J]. 催化学报, 2015, 36(12): 2103-2108.

Tingting Wu, Xiangdong Kang, Mohammad W. Kadi, Iqbal Ismail, Gang Liu, Hui-Ming Cheng . Enhanced photocatalytic hydrogen generation of mesoporous rutile TiO₂ single crystal with wholly exposed {111} facets[J]. Chinese Journal of Catalysis, 2015, 36(12): 2103-2108.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(15)60996-2

https://www.cjcatal.com/CN/Y2015/V36/I12/2103

参考文献

[1] Bae E, Ohno T. Appl Catal B, 2009, 91: 634
[2] Jiao W, Wang L Z, Liu G, Lu G Q, Cheng H M. ACS Catal, 2012, 2: 1854
[3] Liu M, Piao L Y, Zhao L, Ju S T, Yan Z J, He T, Zhou C L, Wang W J. Chem Commun, 2010, 46: 1664
[4] Pan J, Liu G, Lu G Q, Cheng H M. Angew Chem Int Ed, 2011, 50: 2133
[5] Zhao X W, Jin W Z, Cai J G, Ye J F, Li Z H, Ma Y R, Xie J L, Qi L M. Adv Funct Mater, 2011, 21: 3554
[6] Chen X B, Shen S H, Guo L J, Mao S S. Chem Rev, 2010, 110: 6503
[7] Zheng Y, Pan Z M, Wang X C. Chin J Catal (郑云,潘志明,王心晨. 催化学报), 2013, 34: 524
[8] Yang H G, Sun C H, Qiao S Z, Zou J, Liu G, Smith S C, Cheng H M, Lu G Q. Nature, 2008, 453: 638
[9] Han X G, Kuang Q, Jin M S, Xie Z X, Zheng L S. J Am Chem Soc, 2009, 131: 3152
[10] Liu S W, Yu J G, Jaroniec M. J Am Chem Soc, 2010, 132: 11914
[11] Yang H G, Liu G, Qiao S Z, Sun C H, Jin Y G, Smith S C, Zou J, Cheng H M, Lu G Q. J Am Chem Soc, 2009, 131: 4078
[12] Liu G, Yang H G, Pan J, Yang Y Q, Lu G Q, Cheng H M. Chem Rev, 2014, 114: 9559
[13] Wu Q, Wu Z J, Li Y L, Gao H T, Piao L Y, Zhang T H, Du L X. Chin J Catal (吴谦,吴志娇,李永良,高洪涛,朴玲钰,张天慧,杜利震.催化学报), 2012, 33: 1743
[14] Xu H, Reunchan P, Ouyang S, Tong H, Umezawa N, Kako T, Ye J H. Chem Mater, 2013, 25: 405
[15] Xu H, Ouyang S, Li P, Kako T, Ye J. ACS Appl Mater Interfaces, 2013, 5: 1348
[16] Crossland E J W, Noel N, Sivaram V, Leijtens T, Alexander-Webber J A, Snaith H J. Nature, 2013, 495: 215
[17] Li W, Wu Z X, Wang J X, Elzatahry A A, Zhao D Y. Chem Mater, 2013, 26: 287
[18] Jiao W, Xie Y P, Chen R Z, Zhen C, Liu G, Ma X L, Cheng H M. Chem Commun, 2013, 49: 11770
[19] Zheng X L, Lv Y Y, Kuang Q, Zhu Z L, Long X, Yang S H. Chem Mater, 2014, 26: 5700
[20] Maeda K. Chem Commun, 2013, 49: 8404
[21] Zheng X L, Kuang Q, Yan K Y, Qiu Y C, Qiu J H, Yang S H. ACS Appl Mater Interfaces, 2013, 5: 11249
[22] Fang W Q, Huo Z Y, Liu P R, Wang X L, Zhang M, Jia Y, Zhang H M, Zhao H J, Yang H G, Yao X D. Chem Eur J, 2014, 20: 11439
[23] Lai Z C, Peng F, Wang H J, Yu H, Zhang S Q, Zhao H J. J Mater Chem A, 2013, 1: 4182

{111}晶面暴露对介孔金红石TiO₂单晶光催化产氢的促进作用

Enhanced photocatalytic hydrogen generation of mesoporous rutile TiO₂ single crystal with wholly exposed {111} facets

PDF

可视化

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	赵彬彬, 钟威, 陈峰, 王苹, 别传彪, 余火根. 高晶化g-C₃N₄光催化剂: 合成、结构调控和光催化产氢[J]. 催化学报, 2023, 52(9): 127-143.
[2]	蔡铭洁, 刘艳萍, 董珂欣, 陈晓波, 李世杰. 漂浮型Bi₂WO₆/C₃N₄/碳布S型异质结光催化材料用于高效净化水体环境[J]. 催化学报, 2023, 52(9): 239-251.
[3]	刘博文, 蔡家杰, 张建军, 谭海燕, 程蓓, 许景三. MOF/CdS梯型光催化剂同时进行苯甲醇氧化和析氢反应及其机理研究[J]. 催化学报, 2023, 51(8): 204-215.
[4]	乔秀清, 李晨, 王紫昭, 侯东芳, 李东升. TiO_2-_x@C/MoO₂肖特基结: 合理设计及高效电荷分离提升光催化性能[J]. 催化学报, 2023, 51(8): 66-79.
[5]	袁鑫, 范海滨, 刘杰, 覃龙州, 王剑, 段秀, 邱江凯, 郭凯. 连续流技术在光氧化还原催化转化的最新进展[J]. 催化学报, 2023, 50(7): 175-194.
[6]	刘德法, 孙彬, 白硕杰, 高婷婷, 周国伟. 双助催化剂Ag/Ti₃C₂/TiO₂分层花状微球用于增强光催化产氢活性[J]. 催化学报, 2023, 50(7): 273-283.
[7]	Mengistu Tulu Gonfa, 申升, 陈浪, 胡彪, 周威, 白张君, 区泽堂, 尹双凤. 光催化苯制苯酚的研究进展[J]. 催化学报, 2023, 49(6): 16-41.
[8]	李宁, 高雪云, 苏俊珲, 高旸钦, 戈磊. 类金属WO₂/g-C₃N₄复合光催化剂的构造及其优异的光催化性能[J]. 催化学报, 2023, 47(4): 161-170.
[9]	解志鹏, 杨修贝, 张沛, 柯夏婷, 袁昕, 翟黎鹏, 王文滨, 秦娜, 崔乘幸, 屈凌波, 陈雄. 具有可控载流子动力学的烯烃连接的共价有机框架用于高效太阳能光催化制氢[J]. 催化学报, 2023, 47(4): 171-180.
[10]	聂超, 龙向东, 刘琪, 王嘉, 展飞, 赵泽伦, 李炯, 席永杰, 李福伟. 原子分散Ru-P-Ru催化剂的制备及其在多类加氢中的高效应用[J]. 催化学报, 2023, 45(2): 107-119.
[11]	王伟康, 梅少斌, 蒋浩朋, 王乐乐, 唐华, 刘芹芹. 二氧化钛基S型异质结光催化剂的研究进展[J]. 催化学报, 2023, 55(12): 137-158.
[12]	朱可涵, 蒋海凤, 陈高锋, 吴昊, 丁良鑫, 王海辉. 耦合氨氧化和水还原反应实现电化学共合成硝酸盐和氢气[J]. 催化学报, 2023, 55(12): 216-226.
[13]	伍超, 吕康乐, 李鑫, 李覃. 光催化产氢双助催化剂: 类别、合成和设计策略[J]. 催化学报, 2023, 54(11): 137-160.
[14]	王宁宁, 王硕, 李灿, 李晨阳, 刘春江, 陈闪山, 章福祥. ZrO₂修饰均匀氮掺杂氧化物MgTa₂O_6-_xN_x以提升其光催化分解水性能[J]. 催化学报, 2023, 54(11): 220-228.
[15]	宋少青. 晶格匹配的异质结构用于电催化水解离制氢能[J]. 催化学报, 2023, 53(10): 31-33.