锐钛矿/金红石TiO2相结界面电荷分离的时间分辨发光光谱研究

doi:10.1016/S1872-2067(16)62574-3

催化学报 ›› 2016, Vol. 37 ›› Issue (12): 2059-2068.DOI: 10.1016/S1872-2067(16)62574-3

锐钛矿/金红石TiO₂相结界面电荷分离的时间分辨发光光谱研究

王秀丽, 沈帅, 冯兆池, 李灿

中国科学院大连化学物理研究所催化基础国家重点实验室, 洁净能源国家实验室(筹), 辽宁大连 116023

收稿日期:2016-09-12 修回日期:2016-10-15 出版日期:2016-12-27 发布日期:2016-12-27
通讯作者: Can Li
基金资助:
国家自然科学基金（21203185，21373209）和国家重点基础研究发展计划（2014CB239400）.

Time-resolved photoluminescence of anatase/rutile TiO₂ phase junction revealing charge separation dynamics

Xiuli Wang, Shuai Shen, Zhaochi Feng, Can Li

State Key Laboratory of Catalysis, Dalian National Laboratory for Clean Energy, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, Liaoning, China

Received:2016-09-12 Revised:2016-10-15 Online:2016-12-27 Published:2016-12-27
Contact: Can Li
Supported by:
This work was supported by the National Natural Science Foundation of China (21203185, 21373209) and the National Basic Research Program of China (2014CB239400).

摘要/Abstract

摘要：

“结”的构筑，被证实是提高电荷分离效率的重要策略，在太阳电池、光催化等领域有广泛应用.跟踪研究异质结、异相结处的电荷转移动力学，可深入认识结的作用，进一步指导新材料、新结构的设计合成.锐钛矿/金红石TiO₂异相结，可大大提高TiO₂光催化重整生物质制氢的产氢性能.锐钛矿/金红石异相结处的电荷分离、复合等动力学行为还亟需进一步深入研究，我们使用时间分辨发光光谱技术，重点研究了锐钛矿和金红石界面处的电荷转移过程及其对电荷复合过程的影响机制.
我们制备了一系列具有不同晶相组成的TiO₂催化剂，使用XRD和表面灵敏的紫外拉曼光谱表征确定了样品的表面和体相组成，研究其光致发光性质并与其晶相组成相关联.发现，TiO₂的发光行为与其晶相结构直接相关，特别是与其表面晶相结构存在密切关系.其中，500 nm的可见发光带与锐钛矿晶相相关，而835 nm的近红外发光带与金红石晶相相关.分析可见发光带强度随TiO₂晶相组成的变化，发现TiO₂粒子中存在少量金红石成分时，可见发光带强度不仅未猝灭，反而有一个明显的增强效应，同时，近红外发光峰的出现也存在一定的延后现象.这些结果表明锐钛矿/金红石异相结处存在金红石向锐钛矿的电荷转移过程.
进一步，使用时间分辨发光光谱研究可见发光带和近红外发光带的衰减动力学，从而分析揭示锐钛矿/金红石相结对锐钛矿和金红石的载流子动力学的影响机制.对于可见发光带来说，锐钛矿/金红石异相结的存在使可见发光带的衰减速率在微秒时间尺度减慢，而在毫秒时间尺度反而衰减变快.在金红石为主要晶相的混相氧化钛中（如TiO₂-800），还观测到了一个新的约0.43 μs的快衰减成分，表明锐钛矿向金红石的载流子转移过程.对于近红外发光带来说，与可见发光带类似，在微秒时间尺度的衰减也明显变慢，寿命可增长一倍以上，而在毫秒时间尺度的衰减速率没有明显变化.特别是，在锐钛矿/金红石异相结存在条件下，除长于40 μs的微秒衰减成分外，基本所有混相TiO₂样品都显示出~2 μs的快衰减成分，且此快衰减成分的比例受样品晶相组成、制备方法等影响，可达到22%左右.这一快衰减成分的出现，证明了锐钛矿/金红石异相结处存在金红石向锐钛矿的载流子转移过程.
我们通过发光光谱技术研究了锐钛矿/金红石异相结在电荷分离复合过程中的作用.研究发现，锐钛矿/金红石相结存在条件下，可见和近红外发光带都出现了一个新的快衰减成分，证明相结处存在快速的电荷分离过程.由于相结促进电荷分离，在微秒时间尺度抑制了电荷复合，从而使发光衰减明显变慢.而在毫秒时间尺度，电荷复合速率并没有抑制效果.因此，我们提出锐钛矿/金红石相结对光催化活性的促进作用，主要是因为微秒时间尺度促进电荷的有效分离，从而使微秒时间尺度存在更大量的光生电荷参与光催化过程.

关键词: 氧化钛, 锐钛矿/金红石相结, 电荷分离, 电荷复合, 时间分辨发光光谱

Abstract:

Junctions are an important structure that allows charge separation in solar cells and photocatalysts. Here, we studied the charge transfer at an anatase/rutile TiO₂ phase junction using time-resolved photoluminescence spectroscopy. Visible (~500 nm) and near-infrared (NIR,~830 nm) emissions were monitored to give insight into the photoinduced charges of anatase and rutile in the junction, respectively. New fast photoluminescence decay components appeared in the visible emission of rutile-phase dominated TiO₂ and in the NIR emission of many mixed phase TiO₂ samples. The fast decays confirmed that the charge separation occurred at the phase junction. The visible emission intensity from the mixed phase TiO₂ increased, revealing that charge transfer from rutile to anatase was the main pathway. The charge separation slowed the microsecond time scale photoluminescence decay rate for charge carriers in both anatase and rutile. However, the millisecond decay of the charge carriers in anatase TiO₂ was accelerated, while there was almost no change in the charge carrier dynamics of rutile TiO₂. Thus, charge separation at the anatase/rutile phase junction caused an increase in the charge carrier concentration on a microsecond time scale, because of slower electron-hole recombination. The enhanced photocatalytic activity previously observed at anatase/rutile phase junctions is likely caused by the improved charge carrier dynamics we report here. These findings may contribute to the development of improved photocatalytic materials.

Key words: Titanium dioxide (TiO₂), Anatase/rutile phase junction, Charge separation, Charge recombination, Time-resolved photoluminescence

王秀丽, 沈帅, 冯兆池, 李灿. 锐钛矿/金红石TiO₂相结界面电荷分离的时间分辨发光光谱研究[J]. 催化学报, 2016, 37(12): 2059-2068.

Xiuli Wang, Shuai Shen, Zhaochi Feng, Can Li. Time-resolved photoluminescence of anatase/rutile TiO₂ phase junction revealing charge separation dynamics[J]. Chinese Journal of Catalysis, 2016, 37(12): 2059-2068.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(16)62574-3

https://www.cjcatal.com/CN/Y2016/V37/I12/2059

参考文献

[1] G. Dennler, M. C. Scharber, C. J. Brabec, Adv. Mater., 2009, 21, 1323-1338.
[2] H. L. Wang, L. S. Zhang, Z. G. Chen, J. Q. Hu, S. J. Li, Z. H. Wang, J. S. Liu, X. C. Wang, Chem. Soc. Rev., 2014, 43, 5234-5244.
[3] R. Marschall, Adv. Funct. Mater., 2014, 24, 2421-2440.
[4] S. J. A. Moniz, S. A. Shevlin, D. J. Martin, Z. X. Guo, J. W. Tang, Energy Environ. Sci., 2015, 8, 731-759.
[5] M. C. Xu, Y. K. Gao, E. M. Moreno, M. Kunst, M. Muhler, Y. M. Wang, H. Idriss, C. Wöll, Phys. Rev. Lett., 2011, 106, 138302/1-138302/4.
[6] M. Murdoch, G. I. N. Waterhouse, M. A. Nadeem, J. B. Metson, M. A. Keane, R. F. Howe, J. Llorca, H. Idriss, Nat. Chem., 2011, 3, 489-492.
[7] I. Bilecka, P. J. Barczuk, J. Augustynski, Electrochim. Acta, 2010, 55, 979-984.
[8] R. G. Li, Y. X. Weng, X. Zhou, X. L. Wang, Y. Mi, R. F. Chong, H. X. Han, C. Li, Energy Environ. Sci., 2015, 8, 2377-2382.
[9] K. Maeda, Chem. Commun., 2013, 49, 8404-8406.
[10] T. Ohno, K. Tokieda, S. Higashida, M. Matsumura, Appl. Catal. A, 2003, 244, 383-391.
[11] Q. Xu, Y. Ma, J. Zhang, X. L. Wang, Z. C. Feng, C. Li, J. Catal., 2011, 278, 329-335.
[12] J. Zhang, Q. Xu, Z. C. Feng, M. J. Li, C. Li, Angew. Chem. Int. Ed., 2008, 47, 1766-1769.
[13] D. C. Hurum, A. G. Agrios, K. A. Gray, T. Rajh, M. C. Thurnauer, J. Phys. Chem. B, 2003, 107, 4545-4549.
[14] X. R. Zhang, Y. H. Lin, D. Q. He, J. F. Zhang, Z. Y. Fan, T. F. Xie, Chem. Phys. Lett., 2011, 504, 71-75.
[15] G. H. Li, C. P. Richter, R. L. Milot, L. Cai, C. A. Schmuttenmaer, R. H. Crabtree, G. W. Brudvig, V. S. Batista, Dalton Trans., 2009, 10078-10085.
[16] X. M. Sun, W. L. Dai, G. J. Wu, L. D. Li, N. J. Guan, M. Hunger, Chem. Commun., 2015, 51, 13779-13782.
[17] D. O. Scanlon, C. W. Dunnill, J. Buckeridge, S. A. Shevlin, A. J. Logsdail, S. M. Woodley, C. R. A. Catlow, M. J. Powell, R. G. Palgrave, I. P. Parkin, G. W. Watson, T. W. Keal, P. Sherwood, A. Walsh, A. A. Sokol, Nat. Mater., 2013, 12, 798-801.
[18] V. Pfeifer, P. Erhart, S. Y. Li, K. Rachut, J. Morasch, J. Brötz, P. Reckers, T. Mayer, S. Rühle, A. Zaban, I. M. Sero, J. Bisquert, W. Jaegermann, A. Klein, J. Phys. Chem. Lett., 2013, 4, 4182-4187.
[19] T. Kawahara, Y. Konishi, H. Tada, N. Tohge, J. Nishii, S. Ito, Angew. Chem. Int. Ed., 2002, 41, 2811-2813.
[20] K. Komaguchi, H. Nakano, A. Araki, Y. Harima, Chem. Phys. Lett., 2006, 428, 338-342.
[21] L. Q. Jing, S. D. Li, S. Song, L. P. Xue, H. G. Fu, Sol. Energy Mater. Sol. Cells, 2008, 92, 1030-1036.
[22] S. Shen, X. L. Wang, T. Chen, Z. C. Feng, C. Li, J. Phys. Chem. C, 2014, 118, 12661-12668.
[23] J. Kang, F. M. Wu, S. S. Li, J. B. Xia, J. B. Li, J. Phys. Chem. C, 2012, 116, 20765-20768.
[24] Y. Mi, Y. X. Weng, Sci. Rep., 2015, 5, 11482.
[25] J. T. Carneiro, T. J. Savenije, J. A. Moulijn, G. Mul, J. Phys. Chem. C, 2011, 115, 2211-2217.
[26] A. Kafizas, X. L. Wang, S. R. Pendlebury, P. Barnes, M. Ling, C. Sote-lo-Vazquez, R. Quesada-Cabrera, C. Li, I. P. Parkin, J. R. Durrant, J. Phys. Chem. A, 2016, 120, 715-723.
[27] X. L. Wang, Z. C. Feng, J. Y. Shi, G. Q. Jia, S. Shen, J. Zhou, C. Li, Phys. Chem. Chem. Phys., 2010, 12, 7083-7090.
[28] J. Zhang, M. J. Li, Z. C. Feng, J. Chen, C. Li, J. Phys. Chem. B, 2006, 110, 927-935.
[29] J. Y. Shi, J. Chen, Z. C. Feng, T. Chen, Y. X. Lian, X. L. Wang, C. Li, J. Phys. Chem. C, 2007, 111, 693-699.
[30] J. W. Tang, J. R. Durrant, D. R. Klug, J. Am. Chem. Soc., 2008, 130, 13885-13891.
[31] X. L. Wang, A. Kafizas, X. E. Li, S. J. A. Moniz, P. J. T. Reardon, J. W. Tang, I. P. Parkin, J. R. Durrant, J. Phys. Chem. C, 2015, 119, 10439-10447.
[32] J. Zhang, Q. Xu, Z. C. Feng, M. J. Li, C. Li, Angew. Chem. Int. Ed., 2008, 47, 1766-1769.

锐钛矿/金红石TiO₂相结界面电荷分离的时间分辨发光光谱研究

Time-resolved photoluminescence of anatase/rutile TiO₂ phase junction revealing charge separation dynamics

PDF

可视化

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	邵秀丽, 李可, 李静萍, 程强, 王国宏, 王楷. 揭示NiS@Ta₂O₅纳米纤维中梯型电荷转移路径及光催化CO₂转化性能[J]. 催化学报, 2023, 51(8): 193-203.
[2]	阎菲, 张由子, 刘思碧, 邹睿卿, Jahan B Ghasemi, 李炫华. 供体-受体型卟啉基金属有机框架实现有效电荷分离高效光催化析氢[J]. 催化学报, 2023, 51(8): 124-134.
[3]	乔秀清, 李晨, 王紫昭, 侯东芳, 李东升. TiO_2-_x@C/MoO₂肖特基结: 合理设计及高效电荷分离提升光催化性能[J]. 催化学报, 2023, 51(8): 66-79.
[4]	张海波, 王中辽, 张金锋, 代凯. 金属硫化物基异质结光催化剂: 原理、影响、应用和原位表征[J]. 催化学报, 2023, 49(6): 42-67.
[5]	王伟康, 梅少斌, 蒋浩朋, 王乐乐, 唐华, 刘芹芹. 二氧化钛基S型异质结光催化剂的研究进展[J]. 催化学报, 2023, 55(12): 137-158.
[6]	张纹, 田梦, 焦海淼, 蒋海英, 唐军旺. 高匹配的BiVO₄/WO₃纳米碗异质结光阳极用于高效光电化学分解水[J]. 催化学报, 2022, 43(9): 2321-2331.
[7]	张美玉, 秦朝朝, 孙万军, 董聪朝, 钟俊, 吴凯丰, 丁勇. 双助催化剂负载CdS的能量捕集和电荷分离增强产H₂[J]. 催化学报, 2022, 43(7): 1818-1829.
[8]	王晶晶, 胡程, 张以河, 黄洪伟. CdS压电和应变敏感度调控工程用于压电催化产氢[J]. 催化学报, 2022, 43(5): 1277-1285.
[9]	王集杰, Jittima Meeprasert, 韩哲, 王欢, 冯振东, 汤驰洲, 沙峰, 唐珊, 李冠娜, Evgeny A. Pidko, 李灿. TiO₂负载的高分散Cd团簇催化剂高效催化CO₂加氢制甲醇[J]. 催化学报, 2022, 43(3): 761-770.
[10]	许家超, 高朵朵, 余火根, 王苹, 朱必成, 王临曦, 范佳杰. 新型钯-铜纳米点析氢助催化剂: 优化界面氢脱附以实现高效光催化活性[J]. 催化学报, 2022, 43(2): 215-225.
[11]	周志明, 陈金金, 王擎龙, 蒋兴星, 申燕. 硫化钴装饰BiVO₄光阳极提升其光电化学水分解性能[J]. 催化学报, 2022, 43(2): 433-441.
[12]	万俊, 杨玮洁, 刘佳庆, 孙凯龙, 刘琳, 付峰. 固溶体内电场调控增强Bi₂₄O₃₁Cl_xBr_10‒_x体相电荷流动和光催化活性[J]. 催化学报, 2022, 43(2): 485-496.
[13]	张涛, 韩晓驰, Nhat Truong Nguyen, 杨磊, 周雪梅. 二氧化钛基光催化剂用于二氧化碳还原和太阳燃料的生产[J]. 催化学报, 2022, 43(10): 2500-2529.
[14]	梁子展, 沈荣晨, 张鹏, 李佑稷, 李能, 李鑫. 全有机COF/PUP S型光催化剂分解水制氢的性能研究[J]. 催化学报, 2022, 43(10): 2581-2591.
[15]	Khakemin Khan, 徐丽粉, 石明, 曲江珊, 陶晓萍, 冯兆池, 李灿, 李仁贵. 表面组装钴物种同时促进Cd_0.9Zn_0.1S光催化剂的界面电荷分离和表面反应[J]. 催化学报, 2021, 42(6): 1004-1012.